[1]朱 军,陈 友,唐 平,等.大倾角绝缘子保护锌环的腐蚀特征研究[J].电瓷避雷器,2020,(01):174-179.[doi:10.16188/j.isa.1003-8337.2020.01.029]
 ZHU Jun,CHEN You,TANG Ping,et al.Study on Corrosion Characteristics of Zinc Rings of Large Angle Insulators[J].,2020,(01):174-179.[doi:10.16188/j.isa.1003-8337.2020.01.029]
点击复制

大倾角绝缘子保护锌环的腐蚀特征研究()
分享到:

《电瓷避雷器》[ISSN:1006-6977/CN:61-1281/TN]

卷:
期数:
2020年01期
页码:
174-179
栏目:
绝缘子
出版日期:
2020-02-20

文章信息/Info

Title:
Study on Corrosion Characteristics of Zinc Rings of Large Angle Insulators
作者:
朱 军1 陈 友2 唐 平1 曹晓斌2 曾 奕1 毛 强1
(1.国网四川省电力公司电力科学研究院, 成都 610072; 2.西南交通大学电气工程学院, 成都 610031)
Author(s):
ZHU Jun1 CHEN You2 TANG Ping1 CAO Xiaobin2 ZENG Yi1 MAO Qiang1
(1.Sichuan Electric Power Research Institute, Chengdu 610072, China; 2.Electric Engineering School of Southwest Jiaotong University, Chengdu 610031, China)
关键词:
直流输电线路 绝缘子 腐蚀 锌环 铁帽
Keywords:
DC transmission line insulator corrosion zinc ring insulator cap
DOI:
10.16188/j.isa.1003-8337.2020.01.029
摘要:
直流输电线路绝缘子通过安装锌环以减少金具的腐蚀,保障线路的运行安全。为了研究锌环寿命的影响因素,本文搭建了绝缘子直流腐蚀实验平台,研究了绝缘子处于不同悬挂角度时,其保护锌环的腐蚀特征及影响因素。发现锌环的腐蚀面积随着绝缘子悬挂倾角的增大而减少,腐蚀深度随着倾角的增加而增大,而腐蚀生成物将加速锌环的腐蚀; 绝缘子悬挂倾角增大后,锌环与绝缘子表面存水区域减少,腐蚀电流更加集中是造成该现象的主要原因。同时水流方向和锌环腐蚀生成物堆积更集中,改变了绝缘子表面电场分布,使该区域的电流密度增大,加剧该区域锌环的腐蚀,甚至造成锌环与绝缘子铁帽之间的放电。研究认为,当绝缘子处于大倾角悬挂时,可以增加最低点锌环厚度以提高其使用寿命。该研究成果可为直流输电线路绝缘子金具腐蚀防治提供参考。
Abstract:
The DC transmission line insulators reduce the corrosion of the fittings by installing zinc rings to ensure the safe operation of the lines. In order to study the factors influencing the zinc ring life, an insulator DC corrosion test platform was set up to study the corrosion characteristics and influencing factors of the zinc ring when the insulator at different suspension angles. The corrosion area of the zinc ring was found to decrease with the increase of the dip angle of inclination of the insulator. The depth of corrosion increases with the increase of the angle of inclination, and the corrosion products will accelerate the corrosion of the zinc ring. It is put forward that the increase of the angle of inclination of the insulator reduces the area of storing water between the surface of the zinc ring and the insulator, and the more concentrated corrosion current is the main reason for this phenomenon. At the same time, the zinc corrosion product deposits in the water flow direction are more concentrated, which changes the electric field distribution on the surface of the insulator, increases the current density in the area, intensifies the corrosion of the zinc ring in the area, and even causes the discharge between the zinc ring and the insulator cap. It is proposed that when the insulator is suspended at a large angle, the thickness of the lowest point of zinc ring can be increased to increase its service life. The research results can provide reference for the prevention of the corrosion of the insulators metal fittings of HVDC transmission lines.

参考文献/References:

[1] 饶宏,张东辉,赵晓斌,郭琦.特高压直流输电的实践和分析[J].高电压技术,2015,41(8):2481-2488. RAO Hong, ZHANGDonghui, ZHAO Xiaobin, GUO Qi. Practice and analyses of UHVDC power transmission[J]. High Voltage Engineering, 2015, 41(8): 2481-2488.
[2] 徐政,薛英林,张哲任.大容量架空线柔性直流输电关键技术及前景展望[J].中国电机工程学报,2014, 34(29):5051-5062. XU Zheng, XUE Yinglin, ZHANG Zheren. VSC-HVDC technology suitable for bulk power overhead line transmission[J]. Proceedings of the CSEE, 2014, 34(29): 5051-5062.
[3] 刘振亚.全球能源互联网[M].北京:中国电力出版社,2005.
[4] 陈仕龙,张杰,刘红锐,谢佳伟,侯云川.特高压直流输电线路单端电流方向暂态保护[J].电工技术学报,2016, 31(2):171-177. CHEN Shilong, ZHANG Jie, LIU Hongrui, XIE Jiawei, HOU Yunchuan. A single-ended current direction transient protection of UHVDC transmission line[J]. Transactions of China Electrotechnical Society, 2016, 31(2): 171-177.
[5] 何钢,文习山.重冰区输电线路绝缘子选型问题[J].高压电器,2012, 48(4):97-101. HE Gang, WENXishan. Study on selection of transmission line insulators in severe icing area[J]. High Voltage Apparatus, 2012, 48(4): 97-101.
[6] 王黎明,张福增,周军,毛苏春,龙彪,贾志东,关志成.高海拔地区750 kV输电线路绝缘子选型研究[J].中国电力,2006, 39(1):11-14. WANG Liming, ZHANG Fuzeng, ZHOU Jun, MAO Suchun, LONG Biao, JIA Zhidong, GUAN Zhicheng. Study on selection of 750 kV transmission line insulators in high altitude area[J]. Electric Power, 2006, 39(1): 11-14.
[7] ZHANG Fuzeng, WANG Xin, WANG Liming, GUAN Zhicheng, WEN Hua, LI Ruihai, MA Yi. Effect of arcing on dc flashover performance of contaminated porcelain insulators for various suspension patterns at high altitudes[J]. IEEE Transactions on Dielectrics and Electrical Insulation, 2008, 15(3): 783-791.
[8] 吴光亚,罗兵,王蕙.±800 kV特高压直流绝缘子可靠性分析[J].高电压技术,2008, 34(9):1802-1806. WU Guangya, LUO Bing, WANG Hui. Reliability analysis of ±800 kV UHVDC insulators[J]. High Voltage Engineering, 2008, 34(9): 1802-1806.
[9] 余海翔,陈立,梁家豪.天广直流广州换流站换相失败机理探讨[J].高压电器,2015, 51(3):151-156. YU Haixiang, CHEN Li, LIANG Jiahao. Investigation of commutation failure in Guangzhou converter station of Tian-Guang HVDC project[J]. High Voltage Apparatus, 2015, 51(3): 151-156.
[10] 屠竞哲,张健,刘明松,易俊,贺庆,罗煦之,马士聪,卜广全.风火打捆直流外送系统直流故障引发风机脱网的问题研究[J].电网技术,2015, 39(12):3333-3338. TU Jingzhe, ZHANG Jian, LIU Mingsong, YI Jun, HE Qing, LUO Xuzhi, MA Shicong, BU Guangquan. Study on wind turbine generators tripping caused by HVDC contingencies of Wind-Thermal-Bundled HVDC transmission systems[J]. Power System Technology, 2015, 39(12): 3333-3338.
[11] 程春田,励刚,程雄,申建建,陆建宇.大规模特高压直流水电消纳问题及应用实践[J].中国电机工程学报,2015, 35(3):549-560. CHENG Chuntian, LI Gang, CHENG Xiong, SHEN Jianjian, LU Jianyu. Large-scale ultra high voltage direct current hydropower absorption and its experiences[J]. Proceedings of the CSEE, 2015, 35(3): 549-560.
[12] LUO Ling, WANG Liming, GUAN Zhicheng, ZHANG Fuzeng, LI Licheng. Influence of pin corrosion on mechanical characteristic of UHVDC disc suspension insulators and solutions[J]. IEEE Transactions on Dielectrics and Electrical Insulation, 2015, 22(4): 2242-2251.
[13] ZHANG Fuzeng, LUO Bing, WANG Guoli, LIAO Yifan, LUO Ling. Study of test method for accelerated electrolytic corrosion of iron caps of DC disc porcelain insulators[J]. IEEE Transactions on Dielectrics and Electrical Insulation, 2015, 22(5): 2937-2943.
[14] 罗凌,张福增,王黎明,梅红伟,关志成,李立浧.高压直流瓷和玻璃绝缘子金属附件电解腐蚀实验方法[J].电工技术学报,2015, 30(9):103-111. LUO Ling, ZHANGFuzeng, WANG Liming, MEI Hongwei, GUAN Zhicheng, LI Licheng. Test methods for hardware electrolytic corrosion of porcelain and glass insulators on HVDC transmission lines[J]. Transactions of China Electrotechnical Society, 2015, 30(9): 103-111.
[15] 李锐海,廖一帆,罗凌,曾向君,王国利.特高压直流瓷绝缘子金具电解腐蚀问题研究[J].电瓷避雷器,2015(1):1-6. LI Ruihai, LIAO Yifan, LUO Ling, ZENG Xiangjun, WANG Guoli. Research on hardware electrolytic corrosion problem of ceramic insulators on UHVDC transmission line[J]. Insulators and Surge Arresters, 2015(1): 1-6.
[16] 张福增,廖一帆,罗凌,李锐海,王国利,王义宁.特高压直流瓷绝缘子铁帽加速电腐蚀试验[J].电网技术,2014, 38(2):311-315. ZHANG Fuzeng, LIAO Yifan, LUO Ling, LI Ruihai, WANG Guoli, WANG Yining. Accelerated electrolytic erosion test of metal cap of DC porcelain insulator for UHVDC transmission line[J]. Power System Technology, 2014, 38(2): 311-315.
[17] 高理迎,孙涛,赵江涛,魏杰,周军,王洪.直流盘形悬式瓷绝缘子铁帽采用锌环防电解腐蚀特性的试验研究[J].电网技术,2013, 37(12):3381-3385. GAO Liying, SUN Tao, ZHAO Jiangtao, WEI Jie, ZHOU Jun, WANG Hong. Experimental research on anti-electrolytic corrosion characteristics of insulator cap for DC porcelain cap and pin insulator by zinc collar [J]. Power System Technology, 2013, 37(12): 3381-3385.
[18] 宿志一.直流盘形绝缘子金具腐蚀研究中值得关注的问题[J].电网技术,2013, 37(7):2047-2052. SU Zhiyi. Restudy on electrolytic corrosion on fittings of DC cap and pin insulators[J]. Power System Technology, 2013, 37(7): 2047-2052.
[19] 罗凌,王黎明,关志成,张福增,梅红伟,李立浧.抑制高压直流瓷和玻璃绝缘子铁帽电解腐蚀的保护锌环设计[J].中国电机工程学报,2015, 35(17):4531-4538. LUO Ling, WANG Liming, GUANZhicheng, ZHANG Fuzeng, MEI Hongwei, LI Liying. Designing for the protection Zinc ring to suppress electrolytic corrosion of porcelain and glass insulators'Iron Caps on HVDC transmission lines[J]. Proceedings of the CSEE, 2015, 35(17): 4531-4538.
[20] 罗凌,张福增,李锐海,王黎明,关志成,李立浧.抑制运行V串直流瓷绝缘子铁帽电解腐蚀的马蹄形锌环设计[J].电工技术学报,2015, 30(2):220-228. LUO Ling, ZHANG Fuzeng, LI Ruihai, WANG Liming, GUAN Zhicheng, LI Liying. Design for U-Shaped Zinc ring to restrain electrolytic corrosion of V-String ceramic insulators' Caps for DC system[J]. Transactions of China Electrotechnical Society, 2015, 30(2): 220-228.
[21] LUO Ling, WANG Liming, GUAN Zhicheng, MEI Hongwei. Suppression Method for Electrolytic Corrosion of Porcelain Insulators' Iron Caps on UHVDC Transmission Lines[J]. IEEE Transactions on Dielectrics and Electrical Insulation, 2014, 21(6):2448-2457.
[22] 直流系统用盘形悬式瓷和玻璃绝缘子金属附件加速电解腐蚀试验方法: DL/T 1581—2016 [S].北京:中国电力出版社,2016.

备注/Memo

备注/Memo:
收稿日期:2018-05-15作者简介:朱 军(1985—),男,博士,工程师,主要从事高电压与绝缘技术方面研究。基金项目:国网四川省电力公司科技项目(编号:521997160025)。
更新日期/Last Update: 2020-02-20